Specification
HEXAGON NUT WITH CLAMPING PIECE (NON-METAL INSERT) FINE THREAD
ISO 10512, steel 8, steel 10,galvanised, blue passivated
This International Standard specifies the characteristics of prevailing torque type hexagon regular nuts (with non-metallic insert), style 1, with metric fine pitch thread with nominal thread diameters, D, from 8 mm up to and including 36 mm, in product grade A for sizes, D, up to and including 16 mm and product grade B for sizes, D, above 16 mm, and with property classes 6, 8 and 10. The dimensions of the nuts correspond to those given in ISO 8673 plus prevailing torque feature. In this revised version the normative references are now undated in order to facilitate the unequivocal use of each currently applicable version of a standard. Moreover, the content of the standard has been brought in line with the revised ISO 898-2. This standard is identical to the European Standard EN ISO 10512:2012 in which the International Standard ISO 10512:2012 was adopted without any modifications. This standard has been prepared by ISO/TC 2 "Fasteners" in collaboration with CEN/TC 185 "Fasteners", both secretariats of which are held by DIN. The responsible German standardization committee is Working Committee NA 067-00-03 AA "Verbindungselemente mit metrischem Innengewinde" ("Fasteners with metric internal thread") of the Fasteners Standards Committee (FMV) at DIN.
(bis auf Schlüsselweite austauschbar mit DIN 982 Unterschied: neue SW bei M10, 12, 14 und 22)
Technische Daten für ISO 10512
d mm | M3 | M4 | M5 | M6 | M8 | M10 | M12 | M14 | M16 | M18 | M20 | M24 | M27 | M30 | M36 |
S | 5.5 | 7 | 8 | 10 | 13 | 16 | 18 | 21 | 24 | 27 | 30 | 36 | 41 | 46 | 55 |
E min | 6.08 | 7.74 | 8.87 | 11.05 | 14.38 | 18.9 | 21.1 | 24.49 | 26.75 | 30.14 | 33.53 | 39.98 | 45.63 | 51.28 | 61.31 |
m | 2.7 | 3.2 | 3.5 | 4.5 | 6 | 7 | 9 | 10 | 11 | 14 | 15 | 16 | 19 | 23 | 28 |
h max | 3.9 | 5 | 5 | 6 | 6.76 | 8.56 | 10.23 | 11.23 | 12.42 | 14.9 | 17.8 | 25.5 | 27 | 30 | 36 |
Process flow
Cold forging
Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ tapping ➨lock nut➨make heat treatment(if need) ➨ Finish ➨ Packing
Hot forging
Cutting material ➨ hot forging ➨ turning ➨ tapping ➨ lock nut➨make heat treatment(if need) ➨ Finish ➨ Packing
Product Grade
Class 6 Class 8 Class 10
Materials and Chemical compstition
1008
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Al |
0.06 | 0.06 | 0.33 | 0.013 | 0.003 | 0.01 | 0 | 0.01 | 0.028 |
1035
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.34 | 0.13 | 0.73 | 0.012 | 0.002 | 0.02 | 0.01 | 0.02 |
10B21
CHEMICAL COMPOSI % | ||||||
C | Si | Mn | P | S | Cr | B |
0.2 | 0.04 | 0.81 | 0.017 | 0.007 | 0.017 | 0.0021 |
1045
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.45 | 0.23 | 0.58 | 0.014 | 0.006 | 0.057 | 0.008 | 0.016 |
40CR
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.4 | 0.21 | 0.54 | 0.015 | 0.008 | 0.95 | 0.02 | 0.02 |
35CRMO
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
0.35 | 0.22 | 0.59 | 0.01 | 0.003 | 0.93 | 0.01 | 0.01 | 0.21 |
42CRMO
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
0.42 | 0.27 | 0.92 | 0.013 | 0.004 | 1.01 | 0.03 | 0.04 | 0.2 |
Finish
PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON
PACKING
QBH BULK
20-25KG/CTN,36CTNS/PALLET
20-30KG/BAGS,36BAGS/PALLET
ONE TON/BOXES
50KG/ IRON DRUM,12 IRON DRUMS/PALLET
QBH SMALL PACKING
Packing in small boxes according to customer’s requirements
Packing in plastic bag according to customer’s requirements
QBH PALLET TYPE
SOLID WOOD FUMIGATION PALLET
EURO Pallet
THREE SPLINT PALLET
WOODEN BOX
MECHANICAL PROPERTY
TESTING STANDARD:DIN267- 4 OR ISO898-2
SIZE | CLASS | |||||||||||||||||
04 | 05 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV |
NUT | PROOF LOAD N/mm2 |
HV |
NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 380 | 188 | 302 | NO | THIN NUT | 500 | 272 | 353 | YES | THIN NUT | |||||||
M4 | M7 | |||||||||||||||||
M7 | M10 | |||||||||||||||||
M10 | M16 | |||||||||||||||||
M16 | M39 | |||||||||||||||||
SIZE | CLASS | |||||||||||||||||
4 | 5 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | / | / | / | / | / | 520 | 130 | 302 | NO | 1 | |||||||
M4 | M7 | 580 | ||||||||||||||||
M7 | M10 | 590 | ||||||||||||||||
M10 | M16 | 610 | ||||||||||||||||
M16 | M39 | 510 | 117 | 302 | NO | 1 | 630 | 146 | ||||||||||
SIZE | CLASS | |||||||||||||||||
6 | 8 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 600 | 150 | 302 | NO | 1 | 800 | 180 | 302 | NO | 1 | |||||||
M4 | M7 | 670 | 855 | 200 | ||||||||||||||
M7 | M10 | 680 | 870 | |||||||||||||||
M10 | M16 | 700 | 880 | |||||||||||||||
M16 | M39 | 720 | 170 | 920 | 233 | 353 | YES | |||||||||||
SIZE | CLASS | |||||||||||||||||
8 | 9 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | / | / | / | / | / | 900 | 170 | 302 | NO | 2 | |||||||
M4 | M7 | 915 | 188 | |||||||||||||||
M7 | M10 | 940 | ||||||||||||||||
M10 | M16 | 950 | ||||||||||||||||
M16 | M39 | 890 | 180 | 302 | NO | 2 | 920 | |||||||||||
SIZE | CLASS | |||||||||||||||||
10 | 12 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 1040 | 272 | 353 | YES | 1 | 1140 | 295 | 353 | YES | 1 | |||||||
M4 | M7 | 1040 | 1140 | |||||||||||||||
M7 | M10 | 1040 | 1140 | |||||||||||||||
M10 | M16 | 1050 | 1140 | |||||||||||||||
M16 | M39 | 1060 | / | / | / | / | / | |||||||||||
SIZE | CLASS | |||||||||||||||||
12 | ||||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | ||||||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | |||||||||||||
/ | M4 | 1150 | 272 | 353 | YES | 2 | ||||||||||||
M4 | M7 | 1150 | ||||||||||||||||
M7 | M10 | 1160 | ||||||||||||||||
M10 | M16 | 1190 | ||||||||||||||||
M16 | M39 | 1200 |
The advantages of QBH
MOQ: | 900kg |
Price: | Negotiation |
Standard Packaging: | 25kg Carton+900kg/Pallet or 5KG/CTN |
Delivery Period: | 30days |
Payment Method: | L/C, T/T,OA |
Supply Capacity: | 200TON/MONTH |
Specification
HEXAGON NUT WITH CLAMPING PIECE (NON-METAL INSERT) FINE THREAD
ISO 10512, steel 8, steel 10,galvanised, blue passivated
This International Standard specifies the characteristics of prevailing torque type hexagon regular nuts (with non-metallic insert), style 1, with metric fine pitch thread with nominal thread diameters, D, from 8 mm up to and including 36 mm, in product grade A for sizes, D, up to and including 16 mm and product grade B for sizes, D, above 16 mm, and with property classes 6, 8 and 10. The dimensions of the nuts correspond to those given in ISO 8673 plus prevailing torque feature. In this revised version the normative references are now undated in order to facilitate the unequivocal use of each currently applicable version of a standard. Moreover, the content of the standard has been brought in line with the revised ISO 898-2. This standard is identical to the European Standard EN ISO 10512:2012 in which the International Standard ISO 10512:2012 was adopted without any modifications. This standard has been prepared by ISO/TC 2 "Fasteners" in collaboration with CEN/TC 185 "Fasteners", both secretariats of which are held by DIN. The responsible German standardization committee is Working Committee NA 067-00-03 AA "Verbindungselemente mit metrischem Innengewinde" ("Fasteners with metric internal thread") of the Fasteners Standards Committee (FMV) at DIN.
(bis auf Schlüsselweite austauschbar mit DIN 982 Unterschied: neue SW bei M10, 12, 14 und 22)
Technische Daten für ISO 10512
d mm | M3 | M4 | M5 | M6 | M8 | M10 | M12 | M14 | M16 | M18 | M20 | M24 | M27 | M30 | M36 |
S | 5.5 | 7 | 8 | 10 | 13 | 16 | 18 | 21 | 24 | 27 | 30 | 36 | 41 | 46 | 55 |
E min | 6.08 | 7.74 | 8.87 | 11.05 | 14.38 | 18.9 | 21.1 | 24.49 | 26.75 | 30.14 | 33.53 | 39.98 | 45.63 | 51.28 | 61.31 |
m | 2.7 | 3.2 | 3.5 | 4.5 | 6 | 7 | 9 | 10 | 11 | 14 | 15 | 16 | 19 | 23 | 28 |
h max | 3.9 | 5 | 5 | 6 | 6.76 | 8.56 | 10.23 | 11.23 | 12.42 | 14.9 | 17.8 | 25.5 | 27 | 30 | 36 |
Process flow
Cold forging
Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ tapping ➨lock nut➨make heat treatment(if need) ➨ Finish ➨ Packing
Hot forging
Cutting material ➨ hot forging ➨ turning ➨ tapping ➨ lock nut➨make heat treatment(if need) ➨ Finish ➨ Packing
Product Grade
Class 6 Class 8 Class 10
Materials and Chemical compstition
1008
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Al |
0.06 | 0.06 | 0.33 | 0.013 | 0.003 | 0.01 | 0 | 0.01 | 0.028 |
1035
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.34 | 0.13 | 0.73 | 0.012 | 0.002 | 0.02 | 0.01 | 0.02 |
10B21
CHEMICAL COMPOSI % | ||||||
C | Si | Mn | P | S | Cr | B |
0.2 | 0.04 | 0.81 | 0.017 | 0.007 | 0.017 | 0.0021 |
1045
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.45 | 0.23 | 0.58 | 0.014 | 0.006 | 0.057 | 0.008 | 0.016 |
40CR
CHEMICAL COMPOSI % | |||||||
C | Si | Mn | P | S | Cr | Ni | Cu |
0.4 | 0.21 | 0.54 | 0.015 | 0.008 | 0.95 | 0.02 | 0.02 |
35CRMO
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
0.35 | 0.22 | 0.59 | 0.01 | 0.003 | 0.93 | 0.01 | 0.01 | 0.21 |
42CRMO
CHEMICAL COMPOSI % | ||||||||
C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
0.42 | 0.27 | 0.92 | 0.013 | 0.004 | 1.01 | 0.03 | 0.04 | 0.2 |
Finish
PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON
PACKING
QBH BULK
20-25KG/CTN,36CTNS/PALLET
20-30KG/BAGS,36BAGS/PALLET
ONE TON/BOXES
50KG/ IRON DRUM,12 IRON DRUMS/PALLET
QBH SMALL PACKING
Packing in small boxes according to customer’s requirements
Packing in plastic bag according to customer’s requirements
QBH PALLET TYPE
SOLID WOOD FUMIGATION PALLET
EURO Pallet
THREE SPLINT PALLET
WOODEN BOX
MECHANICAL PROPERTY
TESTING STANDARD:DIN267- 4 OR ISO898-2
SIZE | CLASS | |||||||||||||||||
04 | 05 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV |
NUT | PROOF LOAD N/mm2 |
HV |
NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 380 | 188 | 302 | NO | THIN NUT | 500 | 272 | 353 | YES | THIN NUT | |||||||
M4 | M7 | |||||||||||||||||
M7 | M10 | |||||||||||||||||
M10 | M16 | |||||||||||||||||
M16 | M39 | |||||||||||||||||
SIZE | CLASS | |||||||||||||||||
4 | 5 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | / | / | / | / | / | 520 | 130 | 302 | NO | 1 | |||||||
M4 | M7 | 580 | ||||||||||||||||
M7 | M10 | 590 | ||||||||||||||||
M10 | M16 | 610 | ||||||||||||||||
M16 | M39 | 510 | 117 | 302 | NO | 1 | 630 | 146 | ||||||||||
SIZE | CLASS | |||||||||||||||||
6 | 8 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 600 | 150 | 302 | NO | 1 | 800 | 180 | 302 | NO | 1 | |||||||
M4 | M7 | 670 | 855 | 200 | ||||||||||||||
M7 | M10 | 680 | 870 | |||||||||||||||
M10 | M16 | 700 | 880 | |||||||||||||||
M16 | M39 | 720 | 170 | 920 | 233 | 353 | YES | |||||||||||
SIZE | CLASS | |||||||||||||||||
8 | 9 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | / | / | / | / | / | 900 | 170 | 302 | NO | 2 | |||||||
M4 | M7 | 915 | 188 | |||||||||||||||
M7 | M10 | 940 | ||||||||||||||||
M10 | M16 | 950 | ||||||||||||||||
M16 | M39 | 890 | 180 | 302 | NO | 2 | 920 | |||||||||||
SIZE | CLASS | |||||||||||||||||
10 | 12 | |||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | PROOF LOAD N/mm2 |
HV | NUT | |||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | min | max | HEAT TREATMENT | TYPE | |||||||||
/ | M4 | 1040 | 272 | 353 | YES | 1 | 1140 | 295 | 353 | YES | 1 | |||||||
M4 | M7 | 1040 | 1140 | |||||||||||||||
M7 | M10 | 1040 | 1140 | |||||||||||||||
M10 | M16 | 1050 | 1140 | |||||||||||||||
M16 | M39 | 1060 | / | / | / | / | / | |||||||||||
SIZE | CLASS | |||||||||||||||||
12 | ||||||||||||||||||
PROOF LOAD N/mm2 |
HV | NUT | ||||||||||||||||
> | ≤ | min | max | HEAT TREATMENT | TYPE | |||||||||||||
/ | M4 | 1150 | 272 | 353 | YES | 2 | ||||||||||||
M4 | M7 | 1150 | ||||||||||||||||
M7 | M10 | 1160 | ||||||||||||||||
M10 | M16 | 1190 | ||||||||||||||||
M16 | M39 | 1200 |