JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt

  • JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt
  • JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt
  • JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt
  • JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt
Place of Origin CHINA
Brand Name QBH
Certification ISO9001
Model Number JIS B1180
Minimum Order Quantity 900kg
Price Negotiation
Packaging Details 25KG/CTN,36CTN/PALLET or small packing
Delivery Time 30DAYS
Payment Terms L/C, T/T
Supply Ability 500TON/MONTH

Contact me for free samples and coupons.

Whatsapp:0086 18588475571

Wechat: 0086 18588475571

Skype: sales10@aixton.com

If you have any concern, we provide 24-hour online help.

x
Product Details
Standard JIS B1180 Material Carbon Steel
Size M5-M52 Finish ZP YZP HDG BLACK
Grade 4.8 6.8 8.8 10.9 12.9 Packing Carton And Pallet Or According To The Customer's Requirement
Sample Free Sample Thread Machine Thread
Lead Time Per On Order Quantity Type Hexagon Head
Advantage We Can Manufacture According To Client Design,OEM / ODM / Customized Service Provided Oem Yes,welcome
High Light

JIS B1180 Carbon Steel Bolt

,

CL4.8 Carbon Steel Bolt

,

JIS B1180 Half Thread Bolts
Leave a Message
Product Description

JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt

 

Specification

 

JIS B1180 Small Head Hex Bolts have the smallest width heads of all metric hex bolts/hex head cap screws. The width across flats (wrench size) of the three available sizes is 1 to 3 mm smaller than equal sized DIN 931, ISO 4014 and ANSI B18.2.3.1M bolts, while their head height is slightly larger. Otherwise, like their counterparts, they are partially threaded (PT) or fully threaded (FT) with external machine screw threads; use with both internally threaded holes and nuts. M8 is coarse pitch (1.25 mm) while M10 and M12 are fine pitch (but also 1.25 mm). Supplied in Class 8.8 steel, most are zinc plated to resist the formation of corrosion. Minimum threaded length of partially threaded bolts is related to bolt diameter; fully threaded bolts are also called tap bolts; thread tolerance is 6h for plated and 6g for unplated (plain finish); and threading is standard right-hand. Length is measured from under the head to the tip of the bolt.

 

 

 

JIS B1180 Hexagon Head CL4.8 5.8 6.8 Carbon Steel Bolt 0

 

 

 

 

Legend:

l - length of bolt

Makings:QBH

Steel: 5.6,5.8,8.8,10.9,12.9
Stainless: A2,A4
Plastic: -
Non Ferrous: Brass
Thread: 6g

JIS B 1180:2014 HEXAGON HEAD BOLTS AND HEXAGON HEAD SCREWS

 

 

Screw Thread
d
M1.6 M2 M2.5 M3 (M3.5) M4 M5 M6 M8 M10 M12 (M14) M16 (M18) M20
P Pitch
b L≤125
125＜L≤200
L＞200
c max
min
da max
ds max=nominal size
Grade A min
Grade B min
dw Grade A min
Grade B min
e Grade A min
Grade B min
L1 max
k Nominal Size
Grade A max
min
Grade B max
min
k1 Grade A min
Grade B min
r min
s max=nominal size
Grade A min
Grade B min
0.35 0.4 0.45 0.5 0.6 0.7 0.8 1 1.25 1.5 1.75 2 2 2.5 2.5
9 10 11 12 13 14 16 18 22 26 30 34 38 42 46
15 16 17 18 19 20 22 24 28 32 36 40 44 48 52
28 29 30 31 32 33 35 37 41 45 49 53 57 61 65
0.25 0.25 0.25 0.4 0.4 0.4 0.5 0.5 0.6 0.6 0.6 0.6 0.8 0.8 0.8
0.1 0.1 0.1 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.2 0.2 0.2
2 2.6 3.1 3.6 4.1 4.7 5.7 6.8 9.2 11.2 13.7 15.7 17.7 20.2 22.4
1.6 2 2.5 3 3.5 4 5 6 8 10 12 14 16 18 20
1.46 1.86 2.36 2.86 3.32 3.82 4.82 5.82 7.78 9.78 11.73 13.73 15.73 17.73 19.67
1.35 1.75 2.25 2.75 3.2 3.7 4.7 5.7 7.64 9.64 11.57 13.57 15.57 17.57 19.48
2.27 3.07 4.07 4.57 5.07 5.88 6.88 8.88 11.63 14.63 16.63 19.64 22.49 25.34 28.19
2.3 2.95 3.95 4.45 4.95 5.74 6.74 8.74 11.47 14.47 16.47 19.15 22 24.85 27.7
3.41 4.32 5.45 6.01 6.58 7.66 8.79 11.05 14.38 17.77 20.03 23.36 26.75 30.14 33.53
3.28 4.18 5.31 5.88 6.44 7.5 8.63 10.89 14.2 17.59 19.85 22.78 26.17 29.56 32.95
0.6 0.8 1 1 1 1.2 1.2 1.4 2 2 3 3 3 3 4
1.1 1.4 1.7 2 2.4 2.8 3.5 4 5.3 6.4 7.5 8.8 10 11.5 12.5
1.225 1.525 1.825 2.125 2.525 2.925 3.65 4.15 5.45 6.58 7.68 8.98 10.18 11.715 12.715
0.975 1.275 1.575 1.875 2.275 2.675 3.35 3.85 5.15 6.22 7.32 8.62 9.82 11.285 12.285
1.3 1.6 1.9 2.2 2.6 3 3.74 4.24 5.54 6.69 7.79 9.09 10.29 11.85 12.85
0.9 1.2 1.5 1.8 2.2 2.6 3.26 3.76 5.06 6.11 7.21 8.51 9.71 11.15 12.15
0.68 0.89 1.1 1.31 1.59 1.87 2.35 2.7 3.61 4.35 5.12 6.03 6.87 7.9 8.6
0.63 0.84 1.05 1.26 1.54 1.82 2.28 2.63 3.54 4.28 5.05 5.96 6.8 7.81 8.51
0.1 0.1 0.1 0.1 0.1 0.2 0.2 0.25 0.4 0.4 0.6 0.6 0.6 0.6 0.8
3.2 4 5 5.5 6 7 8 10 13 16 18 21 24 27 30
3.02 3.82 4.82 5.32 5.82 6.78 7.78 9.78 12.73 15.73 17.73 20.67 23.67 26.67 29.67
2.9 3.7 4.7 5.2 5.7 6.64 7.64 9.64 12.57 15.57 17.57 20.16 23.16 26.16 29.16
Length of Thread b
- - - - - - - - - - - - - - -
Screw Thread
d
(M22) M24 (M27) M30 (M33) M36 (M39) M42 (M45) M48 (M52) M56 (M60) M64
P Pitch
b L≤125
125＜L≤200
L＞200
c max
min
da max
ds max=nominal size
Grade A min
Grade B min
dw Grade A min
Grade B min
e Grade A min
Grade B min
L1 max
k Nominal Size
Grade A max
min
Grade B max
min
k1 Grade A min
Grade B min
r min
s max=nominal size
Grade A min
Grade B min
2.5 3 3 3.5 3.5 4 4 4.5 4.5 5 5 5.5 5.5 6
50 54 60 66 - - - - - - - - - -
56 60 66 72 78 84 90 96 102 108 116 - - -
69 73 79 85 91 97 103 109 115 121 129 137 145 153
0.8 0.8 0.8 0.8 0.8 0.8 1 1 1 1 1 1 1 1
0.2 0.2 0.2 0.2 0.2 0.2 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3
24.4 26.4 30.4 33.4 36.4 39.4 42.4 45.6 48.6 52.6 56.6 63 67 71
22 24 27 30 33 36 39 42 45 48 52 56 60 64
21.67 23.67 - - - - - - - - - - - -
21.48 23.48 26.48 29.48 32.38 35.38 38.38 41.38 44.38 47.38 51.26 55.26 59.26 63.26
31.71 33.61 - - - - - - - - - - - -
31.35 33.25 38 42.75 46.55 51.11 55.86 59.95 64.7 69.45 74.2 78.66 83.41 88.16
37.72 39.98 - - - - - - - - - - - -
37.29 39.55 45.2 50.85 55.37 60.79 66.44 71.3 76.95 82.6 88.25 93.56 99.21 104.86
4 4 6 6 6 6 6 8 8 10 10 12 12 13
14 15 17 18.7 21 22.5 25 26 28 30 33 35 38 40
14.215 15.215 - - - - - - - - - - - -
13.785 14.785 - - - - - - - - - - - -
14.35 15.35 17.35 19.12 21.42 22.92 25.42 26.42 28.42 30.42 33.5 35.5 38.5 40.5
13.65 14.65 16.65 18.28 20.58 22.08 24.58 25.58 27.58 29.58 32.5 34.5 37.5 39.5
9.65 10.35 - - - - - - - - - - - -
9.56 10.26 11.66 12.8 14.41 15.46 17.21 17.91 19.31 20.71 22.75 24.15 26.25 27.65
0.8 0.8 1 1 1 1 1 1.2 1.2 1.6 1.6 2 2 2
34 36 41 46 50 55 60 65 70 75 80 85 90 95
33.38 35.38 - - - - - - - - - - - -
33 35 40 45 49 53.8 58.8 63.1 68.1 73.1 78.1 82.8 87.8 92.8
Length of Thread b
- - - - - - - - - - - - - -

 

 

 

 

 

 

Process flow

Cold forging

Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ thread rolling ➨make heat treatment(if need) ➨ Finish ➨ Packing

 

Hot forging

Cutting material ➨ hot forging ➨ turning ➨ shrink diameter(half thread) ➨thread rolling ➨ make heat treatment(if need) ➨ Finish ➨ Packing

 

 

 

 

 

Product Grade

 

Class4.8 Class5.8 Class6.8 Class8.8 Class10.9 Class12.9

NO. Mechanical or
physical property		 Property class
4.6 4.8 5.6 5.8 6.8 8.8 9.8 10.9 12.9/12.9
D≤16mma d＞16mmb d≤16mm
1 Tensile strength
Rm,Mpa		 nom.c 400 500 600 800 900 1000 1200
max. 400 420 500 520 600 800 830 900 1040 1220
2 Lower yield strength
ReL,Mpa		 nom.c 240 —— 300 —— —— —— —— —— —— ——
max. 240 —— 300 —— —— —— —— —— —— ——
3 Stress at 0,2 % nonproportional elongation
Rp0.2,Mpa		 nom.c —— —— —— —— —— 640 640 720 900 1080
max. —— —— —— —— —— 640 660 720 940 1100
4 Stress at 0,0048 d non-proportional elongation for
full-size fasteners
Rpf,Mpa		 nom.c —— 320 —— 400 480 —— —— —— —— ——
max. —— 340e —— 420e 480e —— —— —— —— ——
5 Stress under proof load
Spf,Mpa		 nom. 225 310 280 380 440 580 600 650 830 970
Proof Sp,nom/ReL min Or
strength Sp,nom/Rp0.2min Or
rati Sp,nom/Rpf min
 		 0.94 0.91 0.93 0.9 0.92 0.91 0.91 0.9 0.88 0.88
6 Percentage elongation
after fracture for
machined test pieces,A,%		 min. 22 -— 20 —— —— 12 12 10 9 8
7 Percentage reduction of area after
fracture for machined test pieces,Z,%		 min. —— 52 48 48 44
8 Elongation after fracture for full-size
fasteners,Af		 min. —— 0.24 —— 0.22 0.2 —— —— —— —— ——
9 Head soundness No fracture
10 Vickers hardness, HV,
F≥98N		 min. 120 130 155 160 190 250 255 290 320 385
max. 220g 250 320 335 360 380 435
11 Brinell hardness, HBW
,F=30D²		 min. 114 124 147 152 181 238 242 276 304 366
max. 209g 238 304 318 342 361 414
12 Rockwell hardness,HRB ,
HRB		 min. 67 71 79 82 89 　
max. 95g 99.5 　
Rockwell hardness,
HRC		 min. —— 22 23 28 32 39
max. —— 32 34 37 39 44
13 Surface hardness
HV 0.3		 max. —— h h,j h,j
14 Height of non-decarburized thread zone,E,mm min. —— 1/2H1 2/3H1 3/4H1
Depth of complete decarburization in the
thread,G,mm		 max. —— 0.015
15 Reduction of hardness after retempering,HV max. —— 20
16 Breaking torque,
MB,N·m		 min. —— in accordance with ISO 898-7
17 Impact strength,
KVK,I,J		 min. —— 27 —— 27 27 27 27 m
18 Surface integrity in accordance with ISO 6157-1n ISO 6157-3

a Values do not apply for structural bolting.
b For structural bolting d W M12.
c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5.
d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2.
e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values.
f Proof loads are specified in Tables 5 and 7.
g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum.
h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3.
i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable.
j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable.
k Values are determined at a test temperature of −20 °C, see 9.14.
l Applies to d W 16 mm. m Value for KV is under investigation.
n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser.


 

Materials and Chemical compstition

1008

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Al
0.06 0.06 0.33 0.013 0.003 0.01 0 0.01 0.028

 

 

1035

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.34 0.13 0.73 0.012 0.002 0.02 0.01 0.02

 

 

10B21

CHEMICAL COMPOSI %
C Si Mn P S Cr B
0.2 0.04 0.81 0.017 0.007 0.017 0.0021

 

 

1045

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.45 0.23 0.58 0.014 0.006 0.057 0.008 0.016

 

40CR

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.4 0.21 0.54 0.015 0.008 0.95 0.02 0.02

 

35CRMO

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Mo
0.35 0.22 0.59 0.01 0.003 0.93 0.01 0.01 0.21

 

 

42CRMO

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Mo
0.42 0.27 0.92 0.013 0.004 1.01 0.03 0.04 0.2

 

 

Finish

 

PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON

 

 

 

 

PACKING

QBH BULK

20-25KG/CTN,36CTNS/PALLET

20-30KG/BAGS,36BAGS/PALLET

ONE TON/BOXES

50KG/ IRON DRUM,12 IRON DRUMS/PALLET

 

QBH SMALL PACKING

Packing in small boxes according to customer’s requirements

Packing in plastic bag according to customer’s requirements

 

QBH PALLET TYPE

SOLID WOOD FUMIGATION PALLET

EURO Pallet

THREE SPLINT PALLET

WOODEN BOX

 

 

The advantages of QBH

  • QBH brand sales to the main quality assurance.
  • Years of export trade management, excellent service, word-of-mouth guarantee.
  • By working with TUV,escort for quality.
  • Customization of non-standard parts can be made according to customer's requirements and drawings.
  • For quality customers,we can provide a certain credit period.

 

Tags:

IFI Steel Hex Bolt

ASME Stainless Steel Hex Head Bolts

A490M Steel Hex Bolt