DIN933 Full Thread Hexagon Head CL4.8 Steel Nut Bolts

Place of Origin CHINA
Brand Name QBH
Certification ISO9001
Model Number DIN933
Minimum Order Quantity 900kg
Price 800USD/TON-1300USD/TON
Packaging Details 25KG/CTN,36CTN/PALLET or small packing
Delivery Time 30DAYS
Payment Terms L/C, T/T
Supply Ability 500TON/MONTH
Product Details
Standard DIN933 Material Carbon Steel
Size M6-M64 Finish ZP YZP HDG BLACK
Grade 4.8 6.8 8.8 10.912.9 Packing Carton And Pallet Or According To The Customer's Requirement
Sample Free Sample Thread Machine Thread
Lead Time Per On Order Quantity Type Hexagon Head
Advantage We Can Manufacture According To Client Design,OEM / ODM / Customized Service Provided Oem Yes,welcome
High Light

DIN933 Steel Nut Bolts

,

CL4.8 Steel Nut Bolts

,

DIN 933 Stainless Steel Hex Bolts And Nuts

Leave a Message
Product Description

 

Specification

 

 

 

DIN 933 Hex Head Cap Screws

 

DIN 933 Hex Head Cap Screws are fully threaded, have external coarse machine screw threads and, like other hex head screws, are used with both tapped holes and nuts. Their dimensions are similar to ISO 4017 and are available in Class 8.8, 10.9 and 12.9 steel and Class 70 (A2-70, A4-70) stainless steel; less common stainless steel sizes may be Class 50. Zinc plating protects against corrosion while plain finish is unplated and can rust. A2 stainless steel is considered the same as 18-8 and A4 is essentially 316. Class 8.8 and 10.9 thread tolerance for plain finish is 6g and 6h for plated; stainless steel is 6g; right-hand threads are standard. Also known as hex head bolts and tap bolts, all lengths are fully threaded. Length is measured from under the head to the tip. DIN 933 Hex Head Cap Screws are similar to ISO 4017, JIS B1180 and ANSI B18.2.3.1M. In contrast, DIN 931 is partially threaded and DIN 961 has fine threads. (Note: Thread pitch, the distance between threads, is traditionally omitted for fasteners with coarse threads but is included here for reference.)

 

 

 

DIN 933 - Hexagon head bolts with thread up to head

Current norm: DIN EN 24017
Equivalent norms: ISO 4017; CSN 021103; PN 82105; UNI 5739; EU 24017

DIN933 Full Thread Hexagon Head CL4.8 Steel Nut Bolts 0

 

Legend:

l - length of bolt
d - the nominal diameter of the thread
k - head height
r - radius
e - the diameter of the circumscribed circle (not less than)
s - size hex head turnkey
c - thickness of the mounting collar
a - length undercut

 

Makings:QBH

Steel: 5.6,5.8,8.8,10.9,12.9
Stainless: A2,A4
Plastic: Plastic Pa
Non Ferrous: Brass
Thread: 6g

Table according to DIN 933

Screw Thread
d
M1.6 M2 M2.5 M3 (M3.5) M4 M5 M6 (M7) M8 M10 M12 (M14) M16
P Pitch
a max
c min
max
da max
dw Grade A min
Grade B min
e Grade A min
Grade B min
k Nominal Size  
Grade A min
max
Grade B min
max
k1 min  
r min  
s max=nominal size  
Grade A min
Grade B min
0.35 0.4 0.45 0.5 0.6 0.7 0.8 1 1 1.25 1.5 1.75 2 2
1.05 1.2 1.35 1.5 1.8 2.1 2.4 3 3 3.75 4.5 5.25 6 6
0.1 0.1 0.1 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.15 0.2
0.25 0.25 0.25 0.4 0.4 0.4 0.5 0.5 0.5 0.6 0.6 0.6 0.6 0.8
2 2.6 3.1 3.6 4.1 4.7 5.7 6.8 7.8 9.2 11.2 13.7 15.7 17.7
2.4 3.2 4.1 4.6 5.1 5.9 6.9 8.9 9.6 11.6 15.6 17.4 20.5 22.5
- - - - - 5.7 6.7 8.7 9.4 11.4 15.4 17.2 20.1 22
3.41 4.32 5.45 6.01 6.58 7.66 8.79 11.05 12.12 14.38 18.9 21.1 24.49 26.75
- - - - - 7.5 8.63 10.89 11.94 14.2 18.72 20.88 23.91 26.17
1.1 1.4 1.7 2 2.4 2.8 3.5 4 4.8 5.3 6.4 7.5 8.8 10
0.98 1.28 1.58 1.88 2.28 2.68 3.35 3.85 4.65 5.15 6.22 7.32 8.62 9.82
1.22 1.52 1.82 2.12 2.52 2.92 3.65 4.15 4.95 5.45 6.56 7.68 8.98 10.18
- - - - - 2.6 3.26 3.76 4.56 5.06 6.11 7.21 8.51 9.71
- - - - - 3 3.74 4.24 5.04 5.54 6.69 7.79 9.09 10.29
0.7 0.9 1.1 1.3 1.6 1.9 2.28 2.63 3.19 3.54 4.28 5.05 5.96 6.8
0.1 0.1 0.1 0.1 0.1 0.2 0.2 0.25 0.25 0.4 0.4 0.6 0.6 0.6
3.2 4 5 5.5 6 7 8 10 11 13 17 19 22 24
3.02 3.82 4.82 5.32 5.82 6.78 7.78 9.78 10.73 12.73 16.73 18.67 21.67 23.67
- - - - - 6.64 7.64 9.64 10.57 12.57 16.57 18.48 21.16 23.16

 

Screw Thread
d
(M18) M20 (M22) M24 (M27) M30 (M33) M36 (M39) M42 (M45) M48 (M52)
P Pitch
a max
c min
max
da max
dw Grade A min
Grade B min
e Grade A min
Grade B min
k Nominal Size  
Grade A min
max
Grade B min
max
k1 min  
r min  
s max=nominal size  
Grade A min
Grade B min
2.5 2.5 2.5 3 3 3.5 3.5 4 4 4.5 4.5 5 5
7.5 7.5 7.5 9 9 10.5 10.5 12 12 13.5 13.5 15 15
0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.3 0.3 0.3 0.3 0.3
0.8 0.8 0.8 0.8 0.8 0.8 0.8 0.8 1 1 1 1 1
20.2 22.4 24.4 26.4 30.4 33.4 36.4 39.4 42.4 45.6 48.6 52.6 56.6
25.3 28.2 30 33.6 - - - - - - - - -
24.8 27.7 29.5 33.2 38 42.7 46.5 51.1 55.9 59.9 64.7 69.4 74.2
30.14 33.53 35.72 39.98 - - - - - - - - -
29.56 32.95 35.03 39.55 45.2 50.85 55.37 60.79 66.44 71.3 76.95 82.6 88.25
11.5 12.5 14 15 17 18.7 21 22.5 25 26 28 30 33
11.28 12.28 13.78 14.78 - - - - - - - - -
11.72 12.72 14.22 15.22 - - - - - - - - -
11.15 12.15 13.65 14.65 16.65 18.28 20.58 22.08 24.58 25.58 27.58 29.58 32.5
11.85 12.85 14.35 15.35 17.35 19.12 21.42 22.92 25.42 26.42 28.42 30.42 33.5
7.8 8.5 9.6 10.3 11.7 12.8 14.4 15.5 17.2 17.9 19.3 20.9 22.8
0.6 0.8 0.8 0.8 1 1 1 1 1 1.2 1.2 1.6 1.6
27 30 32 36 41 46 50 55 60 65 70 75 80
26.67 29.67 31.61 35.38 - - - - - - - - -
26.15 29.16 31 35 40 45 49 53.8 58.8 63.1 68.1 73.1 78.1

 

 

 

 

 

 

 

Process flow

 

 

Cold forging

Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ thread rolling ➨make heat treatment(if need)Finish Packing

 

Hot forging

Cutting material hot forging turning ➨ shrink diameter(half thread) ➨thread rolling make heat treatment(if need)Finish Packing

 

 

 

 

 

Product Grade

 

Class4.8 Class5.8 Class6.8 Class8.8 Class10.9 Class12.9

NO. Mechanical or
physical property
Property class
4.6 4.8 5.6 5.8 6.8 8.8 9.8 10.9 12.9/12.9
D≤16mma d>16mmb d≤16mm
1 Tensile strength
Rm,Mpa
nom.c 400 500 600 800 900 1000 1200
max. 400 420 500 520 600 800 830 900 1040 1220
2 Lower yield strength
ReL,Mpa
nom.c 240 —— 300 —— —— —— —— —— —— ——
max. 240 —— 300 —— —— —— —— —— —— ——
3 Stress at 0,2 % nonproportional elongation
Rp0.2,Mpa
nom.c —— —— —— —— —— 640 640 720 900 1080
max. —— —— —— —— —— 640 660 720 940 1100
4 Stress at 0,0048 d non-proportional elongation for
full-size fasteners
Rpf,Mpa
nom.c —— 320 —— 400 480 —— —— —— —— ——
max. —— 340e —— 420e 480e —— —— —— —— ——
5 Stress under proof load
Spf,Mpa
nom. 225 310 280 380 440 580 600 650 830 970
Proof Sp,nom/ReL min Or
strength Sp,nom/Rp0.2min Or
rati Sp,nom/Rpf min
 
0.94 0.91 0.93 0.9 0.92 0.91 0.91 0.9 0.88 0.88
6 Percentage elongation
after fracture for
machined test pieces,A,%
min. 22 -— 20 —— —— 12 12 10 9 8
7 Percentage reduction of area after
fracture for machined test pieces,Z,%
min. —— 52 48 48 44
8 Elongation after fracture for full-size
fasteners,Af
min. —— 0.24 —— 0.22 0.2 —— —— —— —— ——
9 Head soundness No fracture
10 Vickers hardness, HV,
F≥98N
min. 120 130 155 160 190 250 255 290 320 385
max. 220g 250 320 335 360 380 435
11 Brinell hardness, HBW
,F=30D²
min. 114 124 147 152 181 238 242 276 304 366
max. 209g 238 304 318 342 361 414
12 Rockwell hardness,HRB ,
HRB
min. 67 71 79 82 89  
max. 95g 99.5  
Rockwell hardness,
HRC
min. —— 22 23 28 32 39
max. —— 32 34 37 39 44
13 Surface hardness
HV 0.3
max. —— h h,j h,j
14 Height of non-decarburized thread zone,E,mm min. —— 1/2H1 2/3H1 3/4H1
Depth of complete decarburization in the
thread,G,mm
max. —— 0.015
15 Reduction of hardness after retempering,HV max. —— 20
16 Breaking torque,
MB,N·m
min. —— in accordance with ISO 898-7
17 Impact strength,
KVK,I,J
min. —— 27 —— 27 27 27 27 m
18 Surface integrity in accordance with ISO 6157-1n ISO 6157-3

a Values do not apply for structural bolting.
b For structural bolting d W M12.
c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5.
d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2.
e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values.
f Proof loads are specified in Tables 5 and 7.
g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum.
h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3.
i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable.
j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable.
k Values are determined at a test temperature of −20 °C, see 9.14.
l Applies to d W 16 mm. m Value for KV is under investigation.
n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser.

 


 

Materials and Chemical compstition

1008

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Al
0.06 0.06 0.33 0.013 0.003 0.01 0 0.01 0.028

 

 

1035

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.34 0.13 0.73 0.012 0.002 0.02 0.01 0.02

 

 

10B21

CHEMICAL COMPOSI %
C Si Mn P S Cr B
0.2 0.04 0.81 0.017 0.007 0.017 0.0021

 

 

1045

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.45 0.23 0.58 0.014 0.006 0.057 0.008 0.016

 

40CR

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu
0.4 0.21 0.54 0.015 0.008 0.95 0.02 0.02

 

35CRMO

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Mo
0.35 0.22 0.59 0.01 0.003 0.93 0.01 0.01 0.21

 

 

42CRMO

CHEMICAL COMPOSI %
C Si Mn P S Cr Ni Cu Mo
0.42 0.27 0.92 0.013 0.004 1.01 0.03 0.04 0.2

 

 

 

 

Finish

 

PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON

 

 

 

 

PACKING

QBH BULK

20-25KG/CTN,36CTNS/PALLET

20-30KG/BAGS,36BAGS/PALLET

ONE TON/BOXES

50KG/ IRON DRUM,12 IRON DRUMS/PALLET

 

QBH SMALL PACKING

Packing in small boxes according to customer’s requirements

Packing in plastic bag according to customer’s requirements

 

QBH PALLET TYPE

SOLID WOOD FUMIGATION PALLET

EURO Pallet

THREE SPLINT PALLET

WOODEN BOX

 

 

The advantages of QBH

  • QBH brand sales to the main quality assurance.
  • Years of export trade management, excellent service, word-of-mouth guarantee.
  • By working with TUV,escort for quality.
  • Customization of non-standard parts can be made according to customer's requirements and drawings.
  • For quality customers,we can provide a certain credit period.
     
  •  

Product application

 

The DIN 933are a hexagon shaped screws, manufactured from steel. Grade 10.9 metric bolts are produced using DIN 933 bolt material such as, either medium carbon steel, medium carbon steel alloy or low carbon boron steel. In order to qualify as a grade DIN 933 bolt 10.9 metric bolts, the allot has to be processed by both quenching as well as tempering. Usually, the DIN 933 bolt 10.9 is used in applications for bolting large and forged parts, and the automotive industry as well.