Roof Mount Solar aluminum 6005 -T5 & stainless steel 304
These are the solution for standing seam metal roof. Comparing with the traditional solution with rail, it is much more economical and much easier for installation. Because it is rail-less and no surface penetration is necessary.
NO. | Mechanical or physical property |
Property class | |||||||||||
4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 9.8 | 10.9 | 12.9/12.9 | |||||
D≤16mma | d>16mmb | d≤16mm | |||||||||||
Supplier | QBH | ||||||||||||
1 | Tensile strength Rm,Mpa |
nom.c | 400 | 500 | 600 | 800 | 900 | 1000 | 1200 | ||||
max. | 400 | 420 | 500 | 520 | 600 | 800 | 830 | 900 | 1040 | 1220 | |||
2 | Lower yield strength ReL,Mpa |
nom.c | 240 | -- | 300 | -- | -- | -- | -- | -- | -- | -- | |
max. | 240 | -- | 300 | -- | -- | -- | -- | -- | -- | -- | |||
3 | Stress at 0,2 % nonproportional elongation Rp0.2,Mpa |
nom.c | -- | -- | -- | -- | -- | 640 | 640 | 720 | 900 | 1080 | |
max. | -- | -- | -- | -- | -- | 640 | 660 | 720 | 940 | 1100 | |||
4 | Stress at 0,0048 d non-proportional elongation for full-size fasteners Rpf,Mpa |
nom.c | -- | 320 | -- | 400 | 480 | -- | -- | -- | -- | -- | |
max. | -- | 340e | -- | 420e | 480e | -- | -- | -- | -- | -- | |||
5 | Stress under proof load Spf,Mpa |
nom. | 225 | 310 | 280 | 380 | 440 | 580 | 600 | 650 | 830 | 970 | |
Proof Sp,nom/ReL min Or strength Sp,nom/Rp0.2min Or rati Sp,nom/Rpf min |
0.94 | 0.91 | 0.93 | 0.9 | 0.92 | 0.91 | 0.91 | 0.9 | 0.88 | 0.88 | |||
6 | Percentage elongation after fracture for machined test pieces,A,% |
min. | 22 | -- | 20 | -- | -- | 12 | 12 | 10 | 9 | 8 | |
7 | Percentage reduction of area after fracture for machined test pieces,Z,% |
min. | -- | 52 | 48 | 48 | 44 | ||||||
8 | Elongation after fracture for full-size fasteners,Af |
min. | -- | 0.24 | -- | 0.22 | 0.2 | -- | -- | -- | -- | -- | |
9 | Head soundness | No fracture | |||||||||||
10 | Vickers hardness, HV, F≥98N |
min. | 120 | 130 | 155 | 160 | 190 | 250 | 255 | 290 | 320 | 385 | |
max. | 220g | 250 | 320 | 335 | 360 | 380 | 435 | ||||||
11 | Brinell hardness, HBW ,F=30D² |
min. | 114 | 124 | 147 | 152 | 181 | 238 | 242 | 276 | 304 | 366 | |
max. | 209g | 238 | 304 | 318 | 342 | 361 | 414 | ||||||
Supplier | QBH | ||||||||||||
12 | Rockwell hardness,HRB , HRB |
min. | 67 | 71 | 79 | 82 | 89 | ||||||
max. | 95g | 99.5 | |||||||||||
Rockwell hardness, HRC |
min. | -- | 22 | 23 | 28 | 32 | 39 | ||||||
max. | -- | 32 | 34 | 37 | 39 | 44 | |||||||
13 | Surface hardness HV 0.3 |
max. | -- | h | h,j | h,j | |||||||
14 | Height of non-decarburized thread zone,E,mm | min. | -- | 1/2H1 | 2/3H1 | 3/4H1 | |||||||
Depth of complete decarburization in the thread,G,mm | max. | -- | 0.015 | ||||||||||
15 | Reduction of hardness after retempering,HV | max. | -- | 20 | |||||||||
16 | Breaking torque, MB,N·m |
min. | -- | in accordance with ISO 898-7 | |||||||||
17 | Impact strength, KVK,I,J |
min. | -- | 27 | -- | 27 | 27 | 27 | 27 | m | |||
18 | Surface integrity in accordance with | ISO 6157-1n | ISO 6157-3 | ||||||||||
a Values do not apply for structural bolting. b For structural bolting d W M12. c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5. d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2. e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values. f Proof loads are specified in Tables 5 and 7. g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum. h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3. i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable. j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable. k Values are determined at a test temperature of −20 °C, see 9.14. l Applies to d W 16 mm. m Value for KV is under investigation. n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser. |
|||||||||||||
Aluminum Solar Roof Clamp Standing seam roof clamp is for tin/metal roof solar rooftop mounting. The solar roof clamps makes mounting on folded seam roof particularly easy. The clamps are simply attached to the standing seams and offer a secure fastening without penetrating on the roof, ensuring great stability with minimum weight. The variety of system combinations allows it to be connected quickly to all rail components. It can also fix panels directly with solar panel clamps.
Six series :6000 series aluminum alloy represents 6061
It contains magnesium and silicon, so it combines the advantages of 4000 series and 5000 series 6061 is a cold-treated aluminum forging product.
It is suitable for applications requiring high resistance to corrosion and oxidation.Good usability, easy coating, good workability.
6063.6061 is the most used.
6063.6060.6463 has low strength in 6 series
6262.6005.6082.6061 has higher strength in 6 series
Scope: vehicle, car luggage rack, door, window, body, heat sink, shell, etc
Applications
⚫ Commercial and residential buildings
⚫ Marine applications and remote areas
Features
⚫ Anodized 6005-T6 aluminum extrusion
⚫ Innovated designed of the Tilt-in modules, which can be pre-assembly with the clamp, make the
installation easy and quick.
⚫ Suitable for difference conditions and the most solar panels at present market.
⚫ Significantly higher strength-to-weight ratio than other framing products, providing improved
efficiency due to greater frame spans, inherent corrosion resistance resulting in low ongoing
maintenance and an extended product life.
⚫ 10 years limited warranty backed up by QBH company
We have high precision CNC lathes to produce different non-standard fastener products, and accept small volume orders as well as special stainless steel materials.will provide you with thoughtful professional service.You will never regret choosing us,we not only have perfect after-sales service,but also have great payment terms!You’re going to see a lot of wins!
JIAXING CITY QUNBANG HARDWARE CO.,LTD is a professional fastener manufacturer and supplier,products are mainly used in the Construction industry, Marine equipment ,solar energy industry, machinery equipment accessories and so on.
FAQ
|
MOQ: | 900KG |
Price: | Negotiation |
Standard Packaging: | BULK or according customer requirement |
Delivery Period: | 30DAYS |
Payment Method: | L/C, T/T,OA |
Supply Capacity: | 200TON/MONTH |
Roof Mount Solar aluminum 6005 -T5 & stainless steel 304
These are the solution for standing seam metal roof. Comparing with the traditional solution with rail, it is much more economical and much easier for installation. Because it is rail-less and no surface penetration is necessary.
NO. | Mechanical or physical property |
Property class | |||||||||||
4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 9.8 | 10.9 | 12.9/12.9 | |||||
D≤16mma | d>16mmb | d≤16mm | |||||||||||
Supplier | QBH | ||||||||||||
1 | Tensile strength Rm,Mpa |
nom.c | 400 | 500 | 600 | 800 | 900 | 1000 | 1200 | ||||
max. | 400 | 420 | 500 | 520 | 600 | 800 | 830 | 900 | 1040 | 1220 | |||
2 | Lower yield strength ReL,Mpa |
nom.c | 240 | -- | 300 | -- | -- | -- | -- | -- | -- | -- | |
max. | 240 | -- | 300 | -- | -- | -- | -- | -- | -- | -- | |||
3 | Stress at 0,2 % nonproportional elongation Rp0.2,Mpa |
nom.c | -- | -- | -- | -- | -- | 640 | 640 | 720 | 900 | 1080 | |
max. | -- | -- | -- | -- | -- | 640 | 660 | 720 | 940 | 1100 | |||
4 | Stress at 0,0048 d non-proportional elongation for full-size fasteners Rpf,Mpa |
nom.c | -- | 320 | -- | 400 | 480 | -- | -- | -- | -- | -- | |
max. | -- | 340e | -- | 420e | 480e | -- | -- | -- | -- | -- | |||
5 | Stress under proof load Spf,Mpa |
nom. | 225 | 310 | 280 | 380 | 440 | 580 | 600 | 650 | 830 | 970 | |
Proof Sp,nom/ReL min Or strength Sp,nom/Rp0.2min Or rati Sp,nom/Rpf min |
0.94 | 0.91 | 0.93 | 0.9 | 0.92 | 0.91 | 0.91 | 0.9 | 0.88 | 0.88 | |||
6 | Percentage elongation after fracture for machined test pieces,A,% |
min. | 22 | -- | 20 | -- | -- | 12 | 12 | 10 | 9 | 8 | |
7 | Percentage reduction of area after fracture for machined test pieces,Z,% |
min. | -- | 52 | 48 | 48 | 44 | ||||||
8 | Elongation after fracture for full-size fasteners,Af |
min. | -- | 0.24 | -- | 0.22 | 0.2 | -- | -- | -- | -- | -- | |
9 | Head soundness | No fracture | |||||||||||
10 | Vickers hardness, HV, F≥98N |
min. | 120 | 130 | 155 | 160 | 190 | 250 | 255 | 290 | 320 | 385 | |
max. | 220g | 250 | 320 | 335 | 360 | 380 | 435 | ||||||
11 | Brinell hardness, HBW ,F=30D² |
min. | 114 | 124 | 147 | 152 | 181 | 238 | 242 | 276 | 304 | 366 | |
max. | 209g | 238 | 304 | 318 | 342 | 361 | 414 | ||||||
Supplier | QBH | ||||||||||||
12 | Rockwell hardness,HRB , HRB |
min. | 67 | 71 | 79 | 82 | 89 | ||||||
max. | 95g | 99.5 | |||||||||||
Rockwell hardness, HRC |
min. | -- | 22 | 23 | 28 | 32 | 39 | ||||||
max. | -- | 32 | 34 | 37 | 39 | 44 | |||||||
13 | Surface hardness HV 0.3 |
max. | -- | h | h,j | h,j | |||||||
14 | Height of non-decarburized thread zone,E,mm | min. | -- | 1/2H1 | 2/3H1 | 3/4H1 | |||||||
Depth of complete decarburization in the thread,G,mm | max. | -- | 0.015 | ||||||||||
15 | Reduction of hardness after retempering,HV | max. | -- | 20 | |||||||||
16 | Breaking torque, MB,N·m |
min. | -- | in accordance with ISO 898-7 | |||||||||
17 | Impact strength, KVK,I,J |
min. | -- | 27 | -- | 27 | 27 | 27 | 27 | m | |||
18 | Surface integrity in accordance with | ISO 6157-1n | ISO 6157-3 | ||||||||||
a Values do not apply for structural bolting. b For structural bolting d W M12. c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5. d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2. e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values. f Proof loads are specified in Tables 5 and 7. g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum. h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3. i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable. j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable. k Values are determined at a test temperature of −20 °C, see 9.14. l Applies to d W 16 mm. m Value for KV is under investigation. n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser. |
|||||||||||||
Aluminum Solar Roof Clamp Standing seam roof clamp is for tin/metal roof solar rooftop mounting. The solar roof clamps makes mounting on folded seam roof particularly easy. The clamps are simply attached to the standing seams and offer a secure fastening without penetrating on the roof, ensuring great stability with minimum weight. The variety of system combinations allows it to be connected quickly to all rail components. It can also fix panels directly with solar panel clamps.
Six series :6000 series aluminum alloy represents 6061
It contains magnesium and silicon, so it combines the advantages of 4000 series and 5000 series 6061 is a cold-treated aluminum forging product.
It is suitable for applications requiring high resistance to corrosion and oxidation.Good usability, easy coating, good workability.
6063.6061 is the most used.
6063.6060.6463 has low strength in 6 series
6262.6005.6082.6061 has higher strength in 6 series
Scope: vehicle, car luggage rack, door, window, body, heat sink, shell, etc
Applications
⚫ Commercial and residential buildings
⚫ Marine applications and remote areas
Features
⚫ Anodized 6005-T6 aluminum extrusion
⚫ Innovated designed of the Tilt-in modules, which can be pre-assembly with the clamp, make the
installation easy and quick.
⚫ Suitable for difference conditions and the most solar panels at present market.
⚫ Significantly higher strength-to-weight ratio than other framing products, providing improved
efficiency due to greater frame spans, inherent corrosion resistance resulting in low ongoing
maintenance and an extended product life.
⚫ 10 years limited warranty backed up by QBH company
We have high precision CNC lathes to produce different non-standard fastener products, and accept small volume orders as well as special stainless steel materials.will provide you with thoughtful professional service.You will never regret choosing us,we not only have perfect after-sales service,but also have great payment terms!You’re going to see a lot of wins!
JIAXING CITY QUNBANG HARDWARE CO.,LTD is a professional fastener manufacturer and supplier,products are mainly used in the Construction industry, Marine equipment ,solar energy industry, machinery equipment accessories and so on.
FAQ